Title: Stability of Solid-State Sintered Li1.5Al0.5Ge1.5(PO4)3 Solid Electrolytes in Various Mediums for All Solid-State Li-ion Batteries
Authors: Dermenci, Kamil Burak
Issue Date: 2020
Abstract: Solid electrolytes are strong candidates for next-generation Li-ion bat-teries for Electrical Vehicle (EV) applications. However, their usage is not widely spread because of their relatively poor ionic conductivity and high electrode/electrolyte interfacial resistance compared to their com-mercial counterparts, organic based liquid electrolytes. Sodium Superi-onic Conductor (NASICON) type solid electrolytes could be an option to overcome these problems. Li1.5Al0.5Ge1.5(PO4)3 (LAGP) stands forward among other NASICON type solid electrolytes with their easy synthesis and processing. Yet, their stability against various mediums remain un-known and needs to be enlightened. In this study, the stability of LAGP against water, air at 85°C and 1M LiOH solution was discussed. LAGP re-sults after sintering at 900°C for 3 hours showed impurity-free, highly dense structure with a restricted grain growth. Water and air aged sam-ples showed a dramatical reduction on grain boundary contribution of to-tal ionic conductivity whereas the sample aged at 1M LiOH solution ex-hibited both reduction in ionic conductivity and increase on grain boundary conductivity. The highest reduction on total ionic conductivity was observed on the sample aged in water. On the contrary, the sample aged in 1M LiOH solution resulted in a net increase on total ionic con-ductivity. The highest total conductivity of 4.3 x 10-4 S/cm was obtained from the sample aged in 1M LiOH. On the other hand, the sample aged the lowest conductivity – 1.8 x 10-4 S/cm – showed the lowest total con-ductivity of all samples.
URI: https://doi.org/10.30939/ijastech..805061
https://app.trdizin.gov.tr/makale/TkRNMU5UY3dNQT09
https://hdl.handle.net/20.500.13087/677
ISSN: 2587-0963
2587-0963
Appears in Collections:TR-Dizin İndeksli Yayınlar Koleksiyonu

Show full item record

CORE Recommender

Page view(s)

26
checked on Oct 3, 2022

Google ScholarTM

Check

Altmetric


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.